■ Application:
DuraZirBeads ®320 :
1.Non-metallic minerals like Calcium Carbonate, kaolin clay, zirconium silicate, TiO2 and other minerals;
2. Metallic minerals like copper, silver, nickel, gold, zinc etc;
3. White pigments, coatings, paints, inks etc;
4. Recommend to be used in stirred mill and ball mill.
DuraZirbeads ®360
1. Non-metallic minerals like Zirconium Silicate, Calcium Carbonate, kaolin clay;
2. Ceramic glazes and frits;
3. Coatings, paints, inks etc;
4. Metallic minerals like copper, silver, nickel, gold, zinc etc;
5. Recommend to be used in stirred mill and ball mill.
DuraZirBeads ®400
1. Non-metallic minerals like Zirconium Silicate,GCC, kaolin clay;
2. Engineering Ceramics.
3. Coatings, paints, inks etc;
4. Metallic minerals like copper, silver, nickel, gold, zinc etc;
5. Metal finishing and polishing.
DuraZirBeads ®420
1.Non-metallic minerals like Calcium Carbonate, kaolin clay, zirconium silicate, TiO2 and other minerals;
2. Dielectric materials, piezoelectric materials, capacitor;
3. Ceramic glazes and frits;
4. Coatings, paints, inks etc;
5. Metallic minerals like copper, silver, nickel, gold, zinc etc;
6. Recommend to be used in stirred mill and ball mill.
■ Specificaton:
|
Specification |
DuraZirBeads ®320 |
DuraZirBeads ®360 |
DuraZirBeads ®400 |
DuraZirBeads ®420 |
|
Chemical composition |
ZrO2 Al2O3 SiO2 etc |
ZrO2 Al2O3 SiO2 etc |
ZrO2 Al2O3 SiO2 etc |
ZrO2 Al2O3 SiO2 etc |
|
Density |
>3.25 |
3.60~3.70 |
>4.0 |
4.20min |
|
Packing Density |
>1.85 |
2.20~2.35 |
>2.35 |
2.85min |
|
Hardness (Mohs) |
8 |
8 |
> 8 |
8min |
|
Roundness |
>90% |
>90% |
>90% |
>90% |
|
Size |
0.2 ~ 12mm, any size breakdown. |
0.2 ~ 12mm, any size breakdown. |
0.4 ~ 13mm, any size breakdown. |
0.2 ~ 12mm, any size breakdown. |
|
Color |
White |
White |
off-white |
White |
■ Packaging:
25kg net in PP-bag or big bag of 500 or 1000kg net. 20-24MT/20'FCL.
■ Key benefits:
•Very High grinding efficiency for superfine grinding.
•Fine chemical stability & contamination-free to the grinded material.
•Extremely low wear rate .
•Excellent combination of toughness and hardness .
•Technical support provided to optimize milling conditions.
|